Fabrication and Characteristics of Anode-Supported Tube for Solid Oxide Fuel Cell

습식법에 의한 고체산화물 연료전지용 연료극 지지체관의 제조 및 특성 연구

To develop anode-supported tubular cell with proper porosity, we have investigated the anode substrate and t the electrolyte-coated anode tube. The anode substrate was manufactured as a function of carbon content in the range of 20 to 50 vol.%. As the carbon COntent increased, the porosity of the anode substrate increased slightly and the carbon c content with proper porosity is found to be 30 vol.%. The anode-supported tube was fabricated by extrusion process a and the electrolyte layer was coated on the anode tube by slurry coating process. The anode-supported tube was cofired successfully at $^1400{\circ}C$ in air. The porosity of the anode tube was 35%. From the gas permeation test, the anode t tube was found to be porous enough for gas supply. On the other hand, the anode-supported tube with electrolyte layer indicated a very low gas permeation rate. This means that the coated electrolyte was dense.

연료극 지지체식 원통형 고체산화물 연료전지를 개방하기 위해 연료극 지지체와 전해질이 코팅된 연료극 원통관의 제조 및 그것의 특성에 대해 연구하였다- 연료극 지지체는 20-50vol.%의 탄소함량에 따라 만들어졌으며, 탄소량이 증가함에 따라 연 료극 지지체의 기공율도 점차 증가하였으며, 적절한 기공율을 가지기 위한 최적 탄소량은 30vol.%임을 확인하였다. 연료극 지지체 관은 압출법으로 제작하였으며, 전해질은 슬러리 코팅법으로 원통판의 바깥쪽에 코팅하였고, $1400^{\circ}C$에서 공소결을 성공적으로 실시하였다. 소결후 물리척특성과 미세구조를 조사하였으며, 연료극 지지체관의 기공율은 35%이었고 연료전지의 요구조건을 만족하였다. 기체투과율 시험을 통하여, 연료극 지지체관 자체는 충분히 다공성을 나타내었으나, 전해질층을 코팅한 경우에는 매우 낮은 기체부과율을 나타냄을 확인하였다. 이것은 코팅된 전해질층이 매우 치밀하다는 것을 의미하며, 본 연구를 통해서 연료극 지지체식 원통형 고체산화물 연료전지가 제조될 수 있음을 확인하였다.