Effects of Polyethylene Addition in Particleboard

파티클보드에 폴리에틸렌 첨가의 효과

Low-density polyethylene (LDPE) powder was investigated as a hydrophobic additive component in particleboard (PB). PBs were manufactured using southern pine particles with a liquid phenolic resin binder at two press temperatures. LDPE at three application rates was used. PBs were tested for physical properties and water soak dimensional stability per the procedure ASTM D 1037. The results indicated that as the LDPE addition level and hot-press temperature were increased, the panel water absorption and thickness swell values decreased. However, the panel's physical properties were affected negatively by increased LDPE application rates. These results indicated that LDPE could be used only in limited amounts to improve the panel's water soak dimensional properties.

저밀도 폴리에틸렌 가루를 실험실 파티클보드의 hydrophobic (소수성) 첨가제로서 사용하였다. Southem pine 파티클과 실험실에서 합성한 페놀수지를 이용하여 2가지 열압온도와 3가지 폴리에틸렌 첨가량으로 파티클보드를 제조하였다. 파티클보드의 밀도, 힘강도, 박리강도 등의 성질과 물에 대한 치수안정화에 대해 성능을 ASTM D 1037과정에 의해서 평가하였다. 평가된 결과는 폴리에틸렌 첨가량과 열압온도가 증가됨에 따라서 두께팽창률과 물흡수율은 감소한다는 것을 보여준다. 그러나 파티클보드의 물리적인 성질은 폴리에틸렌 첨가량이 증가됨에 따라 나쁜 영향을 준다. 이런 결과는 폴리에틸렌이 패널의 안정화를 개선하기 위해 오직 제한된 양만이 사용될 수 있다는 것을 보여준다.