Measurement of Porcelain Shrinkage After Firing Using the Phase-Shifting Profilometry

위상이동 형상측정법을 이용한 도재 소성시의 도재 수축률의 측정

To compare several porcelains made by various manufacturers in shrinkage after firing and investigate the effect of condensation on shrinkage, specimens were prepared and the volume of each body was measured by the phase-shifting profilometry. Baseplate wax was cut by $2.5cm{\times}2cm$ and cast in nonprecious metal(Verabond, U.S.A.), then any surfaces of specimens were abrased and polished on the SiC abrasing papers, preparing 120 specimens. Specimens were divided into six groups according to the porcelain used, and the porcelain used in each group were as follows. Group I : Ceramco dentin porcelain Group B : Creation dentin porcelain Group III : Creation margin porcelain Group IV : Vintage margin porcelain Group V : Vita dentin porcelain Group VI : Vintage dentin porcelain Porcelain was built up on the metal plates using a small spoon and then solution matching to each porcelain was added. The six groups are subdivided into a and b. In subgroup a, only excessive solution was absorbed with tissue and in subgroup b, porcelain was condensed sufficiently. When build-up was completed, the shape was measured using the phase-shifting profilometry. After that, specimens were fired in the furnace programed for each porcelain and then their changed shape were measured again. Using the difference between the two above measurements, the ratio of shrinkage was calculated. Obtained results were as follows ; 1. Regardless of condensation, the volume of fired specimens were not different significantly between the two subgroups a and b in the same group. 2. The ratios of shrinkage were significantly higher in the groups porcelain built-up was condensed than in the groups not condensed 3. The ratios of shrinkage were in the range of 36.81-27.19% in the groups porcelain built up was condensed and 44.52-37.54% in the other groups not condensed.