Abstract
Zn-Ni alloy electrodeposition on steel has been examined by means of X-ray diffraction and scanning electron microscopy. The effect of current density, $Ni^{2+}$ ion concentration, and $Cl^-$ ion concentration on the structure as well as morphology of the electrodeposit have been studied. The Ni content of the electrodeposit increased with decreasing current density in the range studied in this work. The Ni content of the electrodeposit also increased with increasing $Ni^{2+}$ ion and $Cl^-$ ion concentrations. The structure change of the electrodeposit was closely related to the Ni content. In fact, the mixture phase of ${\eta}$ and ${\gamma}$ was found below 10 wt.% of Ni while the ${\gamma}$ phase only was observed above 10 wt.% of Ni. In addition, the lattice parameter, a, of then phase structure increased and the lattice parameter, c, of it decreased as the Ni content of the electrodeposit increased. The morphology of the electrodeposit varied from the plate-like shape to the fine granular shape depending upon the change in composition and structure of the electrodeposit.
Zn-Ni 도금강판의 도금층 구조 및 형상 변화에 미치는 도금 제조 조건중, 전류 밀도, $Ni^{2+}$ 이온 농도, $Cl^-$ 이온 농도 등의 영향에 대하여 고찰하였다. 먼저 도금 조건의 중요한 변수 중의 하나인 전류 밀도를 변화시켰을 때 전류 밀도가 감소함에 따라 도금층 중의 Ni 함량은 증가하였다. 또한 도금 용액 중의 $Cl^-$ 이온과 $Ni^{2+}$ 이온 농도가 증가하면 도금층의 Ni 함량이 증가하였다. 이러한 도금층 중의 Ni 함량은 도금층의 구조 변화와 밀접한 관계를 나타내었다. 즉, Ni 함량이 10 wt.% 미만인 경우에는 ${\eta}$상과 ${\gamma}$상의 혼합 구조를 가지는데 비해서 10 wt.% 이상이 되면 ${\gamma}$단일상으로 변환되었다. 그리고 ${\eta}$상의 구조에서 Ni 함량이 증가함에 따라 a축 방향의 격자 상수는 증가하고 c축 방향의 격자 상수는 감소하였다. 한편 도금층의 형상 변화는 도금층의 조성과 결정구조가 달라짐에 따라 판상의 결정립 형태에서 부터 작은 구상의 입자상에 이르기까지 다양한 변화를 나타내었다.