Abstract
Silicate used as laundry detergent builder was good for pH buffering capacity and solubility but calcium-ion binding capacity and surfactant adsorption ability were lower. As $SiO_2/Na_2O$ molar ratio became higher, pH buffering capacity and ion exchange ability were lower and surfactant adsorption ability was little higher. Anionic surfactant LAS (linear alkylbenzene sulphonate), nonionic surfactant LA-9 (lauryl alcohol EO-9) were used to investigate the detergency performance. Zeolite was better than sodium silicate in detergency performance. In case of LAS, detergency performance was good when $SiO_2/Na_2O$ molar ratio was lower. In case of LA-9, detergency performance was similar without discrimination of molar ratio of $SiO_2/Na_2O$.
수용성 규산나트륨 화합물이 세제용빌더로서 가져야할 특성인 pH 유지능력 및 용해도에 있어서 제올라이트 보다 우수한 성능을 나타냈으나 칼슘이온 결합능 및 계면활성제 흡착능은 낮게 나타났다. 그리고 규산나트륨의 $SiO_2/Na_2O$의 비율이 증가할수록 pH 유지능력과 이온교환 능력은 감소하지만 계면활성제 흡착능력은 다소 증가함을 알 수 있었다. 세제용 계면활성제인 LAS와 LA-9를 사용한 결과 규산나트륨 보다 제올라이트가 세정효율이 높았고, LAS를 사용한 경우 규산나트륨 빌더에서는 $SiO_2/Na_2O$의 비율이 1인 빌더가 세정력이 다소 우수했으며, LA-9인 경우는 $SiO_2/Na_2O$의 비율에 상관없이 비슷한 세정력을 나타내었다.