Abstract
To develop the manufacturing technique for the powder builder of amorphous solid types, the water glass mixed with caustic soda dispersed into the methanol. Thus soluble sodium silicate was made a form of amorphous solid powder. In order to examine characteristics of water soluble sodium silicate $SiO_2/Na_2O$ mol ratio, we investigated solubility, thermogram, SEM, and BET analysis. pH buffering capacity, calcium-ion binding capacity as temperature change, and surfactant loading capacity were examined for characteristics as laundry detergent builder. $SiO_2/Na_2O$ molar ratio of soluble sodium silicate was 1.0, 2.4, 2.8, and zeolite was used in order to investigate basic characteristics of laundry detergent builder. Silicate used with laundry detergent was good for pH buffering capacity and solubility. But calcium-ion binding capacity and surfactant adsorption ability were lower. $SiO_2/Na_2O$ mol ratio became higher, pH buffering capacity and ion exchange ability were lower and surfactant adsorption ability was a little higher.
수용성 규산나트륨 빌더를 개발하기 위하여 물유리와 수산화나륨을 적정비율로 혼합한 후 메탄올에 분산시켜 $SiO_2/Na_2O$의 몰 비율이 2.4∼2.8인 무정형 규산나트륨 고체분말을 제조하였다. 이때 규산나트륨의 $SiO_2/Na_2O$의 몰비, 용해도, thermogram, SEM, BET 등을 통하여 그 물리적 특성을 조사하였으며 빌더로서의 기본적인 특성을 규명하기 위해 $SiO_2/Na_2O$의 몰비가 1.0, 2.4, 2.8인 규산나트륨 빌더와 제올라이트를 사용하여 pH 유지능력, 온도에 따른 칼슘이온 결합능, 계면활성제 흡착능 등을 조사하였다. 그 결과 수용성 규산나트륨 화합물이 세제용빌더로서 가져야할 특성인 pH 유지능력 및 용해도에 있어서 제올라이트 보다 우수한 성능을 나타냈으나 칼슘이온 결합능 및 계면활성제 흡착능은 낮게 나타났으며, 규산나트륨의 $SiO_2/Na_2O$의 비율이 증가할수록 pH 유지능력과 이온교환능력은 감소하지만 계면활성제 흡착능력은 다소 증가함을 알 수 있었다.