Abstract
The permeability of converter slag, replacing material of sand mat on improving soft clay foundation, was evaluated in the laboratory. The effects of grain size, flow water time and aging were investigated using sea and fresh water. In the case of converter slag submerged with fresh water, the coefficients of permeability in A and B samples less than 10 mm grain sizes were measured as $6.52\times10^{-2}cm\; per\; sec\; and\; 5.99\times10^{-1}/cm$ per sec respectively, while they were $1.88\times10^{-2}/cm\; per\; sec,\; 3.86\times10^{-1}/cm$ per sec respectively under sea water condition. Also, the condition of turbulent flow may exit and was experimentally identified from the relationship between hydraulic gradient and seepage velocity. After 100 days under sea water condition, the coefficients of permeability of A and B samples decreased ten times than initial values. The reduction of permeability coefficient was considered to result from the filling of voids in high-calcium quicklime(CaO).
연약지반 개량시 사용되고 있는 샌드매트용 모래의 대체 재료로서 이용 가능성 여부를 전로 슬래그를 대상으로 담수와 해수를 사용하여 입경별, 시간 경과별, 에이징 처리 후 투수계수 변화를 실내시험을 통해 파악하였다. 담수 사용시, 10 mm 미만의 입경을 갖는 A시료와 B시료의 투수계수는 각각 $6.52\times10_{-2}cm/sec,\; 5.99\times10^{-1}cm/sec$으로 측정되는 반면에 해수를 사용할 경우에는 각각 $1.88\times10_{-2}cm/sec,w;3.86\times10^{-1}cm/sec$로 감소하였으며 또한 동수경사와 침투유속의 관계에서 난류흐름이 지배한 것으로 나타났다. 특히, 해수 사용시 100일 동안의 시간경과에 따른 A시료와 B시료의 투수계수는 초기 값보다 1/10배로 감소하는 경향을 보이는데 이는 유리 석회(CaO)에 의한 간극의 막힘 영향으로 확인되었다.