초록
The processing conditions fur the synthesis of platelet W $S_2$ lubricant powder through a solid-gas reaction were optimized. The mixture of tungsten and sulfur powders were sealed in a vacuum of 10$^{-6}$ torr, prior to heat-treating at 85$0^{\circ}C$ fur 8 days. The reaction product showed a well-developed platelet W $S_2$ powder with an average size of 3.8 ${\mu}{\textrm}{m}$. The TGA/DTA analysis of the synthesized W $S_2$ powder was performed up to 120$0^{\circ}C$ at a rate of 1$0^{\circ}C$/min in flowing air (100 ${\mu}{\textrm}{m}$/min) atmosphere. The weight loss was about 6% up to 120$0^{\circ}C$ compared to the original weight. A rapid weight loss of about 5% occurred in the temperature range of 44$0^{\circ}C$ to 66$0^{\circ}C$ and an exothermic peak observed due to the transition of W $S_2$ to W $O_3$. The synthesized W $S_2$powder was coated on the commercial deep grooved ball bearing (No. 6203) to examine the effect of W $S_2$, coating layer on the noise and endurance of the ball bearing. The level of noise obtained from W $S_2$, coated-ball bearing (56 ㏈) was higher. than the value (32 ㏈) occurred in the case of greece lubrication. The endurance of the ball-bearing assembled after the coating of W $S_2$ powder onto each part increased 50 times compared to the non-coated ball-bearing..