초록
In relation to a non-destructive evaluation of irradiation damages, the changes in the hysteresis loop and Barkhausen noise amplitude and the harmonics frequency due to a neutron irradiation were measured and evaluated. The Mn-Mo-Ni low alloy steel of RPV was irradiated to a neutron fluence of 2.3 ×10/sup 19/ n/㎠ (E ≥1 MeV) at 288℃. The saturation magnetization of neutron irradiated metal did not change. The neutron irradiation caused the coercivity to increase, whereas susceptibility to decrease. The amplitude of Barkhausen noise parameters associated with the domain wall motion were decreased by a neutron irradiation. The spectrum of Barkhausen noise is analysed with an applied frequency of 4 Hz and 8 Hz, sampling time of 50 μ sec and 20 μ sec. The harmonic frequency shows 4 Hz, 8 Hz, 12 Hz and 16 Hz reflected from an unirradiated specimen. On the contrary, the harmonic frequency disappeared on the irradiated specimen. In addition to the amplitude, the harmonic frequency of Barkhausen noise is taken into accounts as a promising tool for monitoring the irradiation induced degradation of the reactor materials such as a SA508 of PWR-RPV steel and a Zr₄ of HANARO-CNH.