Abstract
The effects of glass composition on the wettability and reactivity with $ZrO_2$substrate was evaluated and fabrication variables and glass compositions was investigated. Various glass compositions was investigated. Alkaline earth silicate glass show good wettability and lower viscosity and crystallization of glass could be prevented by $B_2O_3$.The sealant glass begin to wet on $ZrO_2$substrate below $900^{\circ}C$ and porosity occurred in various glass compositions, the crystallization and porosity in the glass could be prevented by the addition of flux into glass composition. But flowability and reactivity of glass with $ZrO_2$substrate was enhanced. Processing variables should be optimized to reduce the porosity by enhancing the sintering of glass powder. Many silicate glasses were investigated for the applications of high temperature sealants. Wetting and bonding of glass was good enough to seal together between $ZrO_2$and other ceramic components of SOFC. But porosity and reaction layer were occurred in the sealant glass. It will be possible to produce glass sealant without porosity and reaction layer at the interface by optimization of processing variable and modify the glass compositions. In present study, wettability of glass-filler composite was investigated. The porosity, shape of filler and interfacial reactions of sealant glass with fillers were examined.
지르코니아에 접합과 반응성이 정합되며 고온에서 물리화학적으로 안정성을 갖는 접합재를 제조하기 위하여 silicate계 유리의 조성에 따른 적심특성, 결정화 및 반응성등 제반 특성을 고찰하였다. 지르코니아와의 열팽창계수가 정합 될 수 있는 유리계에 대한 조성 실험하였다. Alkaline earth silicate 유리는 적심성이 우수하였으며 적심각이 낮으며 $B_2O_3$의 첨가함로써 유리의 점도를 조절 및 결정화를 억제할 수가 있었다. $900^{\circ}C$ 이하에서 적심공정에 일어났으며 $800^{\circ}C$에서 10시간동안 유지한 후에 결정화와 계면 반응을 조사한 결과 기공이 많이 발생하였으며 $B_2O_3$를 15mo1% 첨가한 경우 흐름성이 증가하였으며 기판과의 반응성이 높아졌다. 기공을 없애기 위해서는 공정변수를 조절하여 유리의 소결을 촉진할 필요가 있으며 유리점도와 반응성에 관한 최적화가 요구된다. 본 연구에서는 유리-세라믹필러 복합체의 고온적심성에 대하여 조사하였다. Filler로서 $ZrO_2$분말을 여러 조건으로 열처리하여 분말종류와 첨가량에 따라 기공, $ZrO_2$ filler의 형상 및 계면반응 등을 고찰하였다.