Abstract
Measurements of ultrasonic signals caused by partial discharges were perlonnrl by using an ultrasonic measurement technique to diagnose the electrical treeing deterioration in an epoxy mold-type power transformer. We also examined the characteristics of tree growth, partial discharge magnitude and ultrasonic pulse number with the increase of the deterioration time. From these results, it was found that the shape of the tree was a branch-type, and the rates of the tree growth were examined when ac voltages of 16[kV] and 20[kV] were applied Ultrasonic pulse number and discharge magnitude were rapidly increased as the length of the tree grows after the middle stage of the deterioration time, and it appeared that ultrasonic pulse number was proportional to discharge magnitude. Attenuation, time-delaying and directivity characteristics of ultrasonic signals propagated into epoxy resin by using ultrasonic oscillation and receiving systems are also re[prted as a basic data of ultrasonic mesasurements in mold-type power transformer.former.
본 연구는 초음파 측정법을 사용하여 부분방전에 의한 에폭시 몰드형 전력변압기의 열화상태을 진단하기 위해 에폭시수지의 트리진전에 초음파신호를 분석하였으며, 또한 열화시간에 따른 트리길이, 방전전하량 및 초음파 펄스수의 특성을 조사하였다. 실험 결과, 애폭시수지에 발생된 트리는 수지령이면, 인가전압 16[kV]에 대한 트리 길이 및 트리 폭의 평균성 장률은 각각 0.014 및 0.026[mm/min] 이였으며, 20[kV]의 경우 이들 값은 각각 0.032 및 0.063[mm/min]으로 더욱 증가된 것으로 나타났다. 열화중기 이후 트리가 성장함에 따라 초음파 펄스수 및 부분방전 전하량은 급격히 증가된 것으로 나타났다. 그리고 초음파 펄스수는 방전전하량에 비례하여 증가되었다. 또한 몰드형 전력변압기의 초음파 측정시 기본 데이터를 얻기 위해 초음파 발진 및 수신장치를 사용하여 에폭시수지에 대한 초음파신호의 감쇄, 시간지연 및 지향특성도 조사하였다.