Abstract
The characteristics of lubricant for computer hard disk was investigated by surface analysis technique. The bonding state between carbon and lubricant is analysed to indentify the origin of adhesion. It is found that the thickness of lubricant is increased as pulling-up speed becomes faster and lubricant concentration is increased. The dominant surface contaminants on carbon overcoat are identified with C-OH and CO. The bond strength between carbon and lubricant is enhanced with heat treatment.
컴퓨터 하드디스크용 윤활제인 PFPE중 Z-DOL과 AM2001을 이용하여 pulling-up speed와 윤활제의 농도를 변화시키면서 윤활제의 두께변화를 알아보았으며, 또한 열처리를 통해 overcoat층인 carbon과 윤활제의 결합특성을 알아보았다. Pulling-up speed가 빠를수록, 그리고 윤활제의 농도가 증가할수록 윤활제의 두께는 두껍게 coating되었음을 알 수 있었으며, 또한 XPS을 이용하여 분석해 본 결과, overcoat층인 carbon에 존재하는 표면 오염물은 C-OH, CO가 지배적이었고, 열처리를 함으로써 overcoat층인 carbon과 윤활제의 결합력이 증진됨을 알 수 있었다.