Abstract
Bi-doped lanthanum magnetics $(La_{0.67-x}Bi_xCa_{0.33}MnO_3(x\;=\;0,\; 0.04,\; 0.1,\; 0.2))$ samples have been prepared by standard ceramic process. The crystallinity and microstructures of the samples have been investigated by x-ray diffractometry and optical microscopy, respectively. The magnetic and magnetoresistive properties of the samples have been measured by vibrating sample magnetometery and van der Pauw method, respectively, at the temperatures ranging of 100 K~300 K with applied magnetic field of 0.4~0.5 T. Good crystallinity and high Curie temperature (275 K) have been obtained for the Bi-doped samples with small dosage (x = 0.04, 0.1) even they were sintered at 120$0^{\circ}C$, which is about 20$0^{\circ}C$ lower than normal sintering temperature of 140$0^{\circ}C$. The Bi-doped samples with the small dosage showed lower relative electrical resistivity and higher magneto-resistive ratio compared to the undoped sample in the most temperatures measured. The Bi-doped samples also exhibited large magnetoresisitve ratio (maximum of 15% for x = 0.1) at room temperature even under a weak magnetic field of 0.4 T.
란탄 망가나이트에 Bi를 첨가한 벌크 시료(La0.67xBixCa0.33MnO3(x=0, 0.04, 0.1, 0.2)들을 세라믹스 제조공정을 이용하여 제조했다. 제조한 시료들의 결정성과 미세구조를 x-선 회절분석과 광현미경으로 조사하고, 자기 및 자기저항 특성을 100~300K의 온도 범위에서 0.4~0.5T의 자기장을 인가하여 진동시료형자력계와 van der Pauw법으로 조사했다. Bi를 소량(x=0.04, 0.1) 첨가한 시료의 경우 시료를 제조할 수 있었다. 또한 Bi를 소량 첨가하는 것에 의해 측정한 대부분의 온도에서 비저항이 감소하였고 자기저항비가 증가하였다. 아울러 실온에서 약한 자기장(0.4T)하에서도 큰 자기저항비(x=0.1의 경우 15%)를 나타냈다.