(Dept. of Metallurgical Eng., Chungnam National University)
;
(Advanced Fuel Cladding Project, Korea Atomic Energy Research Institute)
To investigate the effects of V and Sb on the recrystallization of Zr-0.8Sn alloy, the microstructure of heat-treated specimens was observed by optical microscope, SEM, and TEM. Microhardness tests were also carried out for the annealed specimens. From microstructural studies, the V or Sb additions were found to delay recrystallization process as well as grain growth. Especially, Sb was more effective in delaying the recrystallization. This delay of recrystallization and grain growth by V or Sb additions may be due to the interference in the movement of dislocation and crystal interface by V or Sb precipitates.
Zr-0.8Sn합금의 재결정에 미치는 V, Sb의 영향을 조사하기 위해 냉간 압연 후 여러 온도 조건에서 열처리된 시편의 미세조직을 편광광학현미경, SEM, TEM으로 관찰하였고 미소경도계로 경도값을 측정하였다. 미세조직을 관찰한 결과 V과 Sb의 첨가에 의해 재결정이 지연되었으며, 재결정 완료 후의 결정립 성장도 억제됨이 관찰되었다. 특히 Sb는 V보다 재결정을 완료하는데 필요한 온도를 상승시키므로 재결정을 지연시키는 효과가 더욱 큰 것으로 생각된다. 이 처럼 첨가원소가 증가함에 따라 재결정에 늦어지고 결정립이 미세화 되는 것은 V이나 Sb 첨가에 의해 형성된 석출물이 전위나 입계의 이동을 방해하기 때문인 것으로 사료된다.