The effects of additives on the Zn electrodeposition in chloride-based electrolyte were investigated using circulation cell with three electrodes system. The cathodic polarization increased with the addition of polyethylenglycol (hereafter PEG) in electrolyte. This was attributed to the adsorption of the additives on the electrode and the inhibition of migration of metal ion. The PEG, however, did not have any noticeable effect on the properties of plating solutions at the concentration used. The effect of PEG on the electrocrystallization was related to its molecular weight. With the increase of molecular weight, the cathodic polarization increased, while the surface roughness was improved with the decrease of brightness. Especially, the PEG mixed with different molecular weights was the most effective. The orientation and the type of the deposited grains were changed and refined by PEG, which resulted in the modification of deposited surface roughness and brightness.
염화물욕 아연도금에서 순환셀 도금장치에 3전극계를 부착하여 첨가제 효과를 조사하였다. 도금액에 폴리에틸렌글리콜(이하 PEG)의 첨가는 도금 과전압을 증가시키고 수소발생을 억제하는데 이것은 첨가제에 의하여 아연 이온의 이동을 억제하거나 음극에 첨가제 흡착에 의한 것으로 생각된다. 그러나 PEG는 사용되는 도금액의 물성(전도도, 점도, 비중)에는 영향을 미치지 않는 것으로 나타났다. 도금층에 미치는 영향은 표면 조도가 개선되고, 광택도가 감소된다. 이러한 영향은 PEG 분자수가 클수록 증가되나 분자수가 다른 PEG의 혼합첨가제에서는 광택도 감소가 줄어든다. 이러한 것은 도금층 결정면의 방향성, 입자의 크기 및 형태가 PEG 분자 수에 따라 다르게 나타나는 것에 기인하는 것으로 판단된다.