Abstract
In the paper, Significant sintering phenomena at refractory temperature ranges, from $1400^{\circ}C$ to $1700^{\circ}C$, of the pure spinel ($MgAl_{2}O_{4}$) and the experimental data from other researchers are analysed and compared in terms of density ($\rho$), grain growth exponent(n), and activation energy (Q). Similar to the density rewsults, the grain growth results above $1600^{\circ}C$ appear similar for the spinel, but for temperatures lower than about $1600^{\circ}C$ results are distinctly differently grouped. However, the grain growth exponents are different, six for the spinel (below $1600^{\circ}C$), and five at high temperatures(above $1600^{\circ}C$), with the activation energy of 474$\pm$38 kJ/mol below $1600^{\circ}C$, which is very close to the published values, 360~580 kJ/mol.
순수 스피넬($MgAl_{2}O_{4}$)에 대하여 내화온도 범위인 $1400^{\circ}C$에서 $1700^{\circ}C$까지의 온도에서 주요 소결현상인 밀도(p), 입성장지수(n), 활성화에너지(Q)를 구하고 다른 실험 data와 비교 분석하였다 $1600^{\circ}C$ 이하의 온도에서 입성장은 밀도와 마찬가지로 스피넬과 비슷하였으나 $1600^{\circ}C$ 이하의 온도에서는 아주 다르게 나타났다. 그러나 입성장지수는 $1600^{\circ}C$이하에서는 스피넬에 대하여 6이었고 $1600^{\circ}C$이상의 높은 온도에서는 5이었다. 활성화 에너지는 $1600^{\circ}C$이하의 온도에서는 474.38 kJ/mol로 종래의 값인 360~580 kJ/mol에 매우 근접하였다.