Studies on the Coating Structure and Printability of Coated Paper(III) - Effect of the interaction with pigments and ionic latices on the property of coated paper -

도공층 구조 및 도공지의 인쇄적성에 관한 연구(제3보) - 도공용 안료와 이온성 라텍스와의 상호작용이 도공지 품질에 미치는 영향 -

This paper was intended to evaluate the effect of the blending condition of pigments on the packing structure of coating color and the interaction between pigments and latices on the optical and interior properties of coated paper. It has been studied many ways to modify the coating structure to induce the interaction among coating components as followings ; 1) to use dispersant for pigment, 2) to control the charge density and the type of surface charge of latex, 3) to support the water retention by adding water retention agent or flow modifier. This paper was performed through the introduction of interaction between pigments which were two kinds of clays and one precipitated calcium carbonate(PCC) and ionic latices of which anionic and amphoteric respectively under the certain blending condition of pigments where their blending ratio of clays to calcium carbonate was 70pph to 30pph. The reason is that packing volume of pigments was highest in that region and thixotropical behavior appears in measuring rheology of coating color. We measured the properties of coating color, interaction with pigments and latex, and properties of coated paper and its printability. As a results, we could find out that amphoteric latex had a great influence on the interaction with pigments, especially clays, no matter what grade and also affected the coating structure significantly in case that this blending condition was 70(clays) to 30(PCC). It produced a powerful effect on the forming of bulky and smooth coating structure and in turn improved the printability of coated paper.

가장 보편적으로 사용되고 있는 도공용 안료인 클레이와 탄산칼슘의 배합비율을 실제 도공공정의 안료 혼합비와 근사하게 설정한 후, 이온성 라텍스를 적용해 봄으로서 이들의 상호작용과 도공지의 품질에 미치는 영향에 대해 검토해 보았다. 1,2급 클레이를 각각 35부, 탄산칼슘을 30부씩 혼합한 후, 제조한 도공액의 탈수량 및 침강중량비 측정 결과, 양성라텍스는 음이온성 라텍스보다 다분산 안료 배합하에서도 안료와의 상호작용이 크다는 것을 알 수 있었으며, 형성된 필터케이크충의 구조가 다공성임을 알 수 있었다. 이러한 결과는 제조한 도공지의 표면거칠기 및 투기도 등의 도공지 표면 및 내부육특성 측정을 통해 확인할 수 있었다. 결과적으로 양성라텍스를 사용하여 제조한 도공지의 인쇄적 성이 음이온성 라텍스를 사용한 경우보다 우수하였다. 이는 양성라텍스가 탄산칼슘이 일정비율 첨가된 안료 배합조건 하에서도 이오기의 전하반전 특성을 통해 클레이와의 정전기적 상호작용을 할 수 있다는 사실을 보여주었으며, 1급 클레이의 혼합비율 일부를 2급 및 탄산칼슘으로 대체하여 도공지의 품질 및 인쇄적성을 개량하였다.