상아질 표면처리방법이 compomer의 전단결합 강도에 미치는 영향에 관한 연구

EFFECT ON THE SHEAR BOND STRENGTH OF A COMPOMER TO DENTIN ACCORDING TO SURFACE CONDITIONING

The purpose of this study was to evaluate the shear bond strength of the Compoglass Carvifil bonded on the dentin surface according to etching or non-etching and two time application or three time application of single component. Human non-carious 60 extracted 3rd molar were used. The occlusal dentin surfaces of all teeth were exposed with Diamond Wheel Saw and polished with Lapping & Polishing machine(South Bay Technology Co., U.S.A). The teeth were then distributed randomly into four groups of 15 teeth each and dentin surface were conditioned as following. Control group : Non-etching, two times application of Syntac Single Component. (According to manufacture's instruction) Experimental group 1 : Non-etching, three times application of Syntac Single Component. Experimental group : 2 Etching, two times application of Syntac Single Component. Experimental group 3 : Etching, three times application of Syntac Single Component. Compoglass were bonded to exposed dentin surfaces and all samples were placed in distilled water for 7 days. The shear bond strengths were measured by universal testing machine (SHIMADAZU AUTOGRAPH, AGS-4D., Japan). The results were as follows : 1. Experimental group 3 revealed the highest value (30.75${\pm}$4.74 MPa) and control group revealed the lowest value(14.85${\pm}$2.69 MPa). There was significant difference of shear bond strength among four groups(P<0.01) 2. The acid-etching groups (experimental group 2, 3) had higher shear bond strengths than non etching groups(control group and experimental group 1). 3. The additional application of Syntac single component groups revealed a higher bond strength than two times application groups (control group and experimental group 2).