극저온액체 저장용기에서 열전도 차폐단의 영향

Effect of Vapor-Cooled Heat Stations in a Cryogenic Vessel

Ni/MH 2차전지의 음극용 금속간화합물전극의 부식특성에 미치는 합금원소와 결합제의 영향을 조사하였다. 전극의 재료는 $(LM)Ni_{4.49}Co_{0.1}Mn_{0.205}Al_{0.205}$와 $(LM)Ni_{3.6}Co_{0.7}Mn_{0.3}Al_{0.4}$의 $AB_5$ type합금을 모재로 하였다. 여기에 Si sealant 또는 PTFE를 결합제로 첨가한 것과 원재료 분말에 구리를 20% 무전해도금한 것을 냉간 압착하여 전극을 제조하였다. 부식특성을 조사하기위해 탈공기된 6M의 KOH 용액에서 동전위법과 순환전위법을 이용하여 부식전류와 전류밀도를 측정하였다. 모재에 Co가 많이 함유되면 전극의 내식성을 향상시키고 Ni이 많이 함유되면 충전과 방전을 반복하는 동안에 전극의 안정성을 저하시켰다. 부식전류밀도는 Si sealant를 결합제로 사용한 전극의 경우가 PTFE를 사용한 전극의 경우보다 낮았고 Cu가 도금된 전극은 내식성에서 가장 우수하게 나타났다.

An experimental study on effect of vapor-cooled heat stations in a 5.5 liter cryogenic vessel has been performed. The cryogenic vessel is made of stainless steel of thickness of 1mm and insulated by the combined insulation of vacuum, MLI(multi-layer insulation) and vapor-cooled radiation shield. Vapor-cooled heat stations are also constructed based on the 1-dimensional thermal analysis to reduce the heat inleak through a filling tube. Thermal analysis indicates that the vapor-cooled heat stations can substantially enhance the performance of vessel for cryogenic fluids with high $C_p/h_{fg}$ where $C_p$ the specific heat and $h_{fg}$ the heat of vaporization, such as $LH_2$ and LHe. The experimental results for $LN_2$ shows that the total heat inleak into inner vessel consists of 14% radiation and 86% conduction through the filling tube. Therefore, it is expected that the conduction heat in leak of the vessel for high $C_p/h_{fg}$ cryogenic fluids can be significantly reduced. powders. The amount of copper coating was 20wt%. In order to examine corrosion behavior of the electrodes, the corrosion current and the current density, in 6M KOH aqueous solution after removal of oxygen in the solution, were measured by potentiodynamic and cyclic voltamo methods. The results showed that Co in the alloy increased corrosion resistance of the electrode whereas Ni decreased the stability of the electrode during the charge-discharge cycles. The electrode used Si sealant as a binder showed a lower corrosion current density than the electrode used PTFE and the electrode used Cu-coated alloy powders showed the best corrosion resistance.