Engineering properties of Permeable Polymer Concrete with Fly Ash and CaCO₃

플라이 애쉬와 탄산칼슘을 혼입(混入)한 투수성(透水性) 폴리머 콘크리트의 공학적(工學的) 성질(性質)

This study was performed to evaluate the engineering properties of permeable polymer concrete with Fly Ash and $CaCo_3$. The following conclusions were drawn; 1. The unit weight was in the range of $1,830{\sim}1,932kgf/m^3$, the unit weights of those concrete were decreased 16~20% than that of the normal cement concrete. 2. The highest strength was achieved by fly ash 50% and $CaCo_3$ 50% filled permeable polymer concrete, it was increased 26% by compressive strength, 121% by tensile strength and 275% by bending strength than that of the normal cement concrete, respectively. 3. The ultrasonic pulse velocity was in the range of 2,805~2,904m/s, which was showed about the same compared to that of the normal cement concrete. Fly ash 50% and $CaCo_3$ 50% filled permeable polymer concrete was showed higher pulse velocity.

이 연구는 폴리머와 충전재를 혼입한 투수성 폴리머 콘크리트의 공학적 성질을 구명한 것으로써, 이 연구를 통해 얻어진 결과를 요약하면 다음과 같다. 1. 단위중량은 $1,830{\sim}1,932kgf/m^3$로써 보통 시멘트 콘크리트에 비해 16~20%정도 감소되었고, 플라이 애쉬만을 충전재로 사용한 투수성 폴리머 콘크리트에서 가장 작게 나타났다. 2. 강도는 플라이 애쉬와 탄산칼슘의 양이 같은 투수성 폴리머 콘크리트에서 가장 크게 나타났고, 보통 시멘트 콘크리트보다 압축강도에서는 26%, 인장강도에서는 121%, 휨강도에서는 275%가 증가되었으며, 압축강도에 대한 인장강도와 휨강도비가 보통 시멘트 콘크리트보다 2.5배와 3.5배이상 크게 나타나 취성이 크다는 것을 알 수 있다. 3. 초음파진동속도는 2,805~2,904m/s로써 보통 시멘트 콘크리트와 거의 비슷하게 나타났으며, 충전재별로는 플라이 애쉬와 탄산칼슘을 같은 양으로 혼입한 투수성 폴리머 콘크리트에서 비교적 큰 값을 보였다.