Effect of Supporting Anions on Particle Characteristics of Barium Titanyl Oxalate Formed by Homogeneous Precipitation

지지 음이온이 균일 침전법에 의해 생성된 Barium Titanyl Oxalate의 입자특성에 미치는 영향

Spherical, ${\mu}m$-sized particles of barium titanyl oxalate were prepared by thermal decomposition of dimethyl oxalate in acidic barium and titanium solutions. Precipitation was carried out in the presence of several supporting anions. Spherical particles having a specific type of particle size distribution. i.e., unimodal or bimodal distribution, with mean size in the range of $0.2{\sim}3{\mu}m$, were formed depending on the supporting anions, oxalate ion generation rate and aging time. Particles of barium titanyl oxalate settled on the bottom of the beaker at the aging time of 120 min grew to the critical monosize of about $1.5{\sim}3{\mu}m$. XRD spectra and chemical analyses of barium titanate showed that barium titanyl oxalate with high qualities could be synthesized by choosing chloride ion as a supporting anion and increasing the reaction temperatures.

$Ba^{2+}$와 $Ti^{4+}$이온의 산성용액에서 dimethyl oxalate의 열분해에 의해서 구형이고 ${\mu}m$크기의 barium titanyl oxalate입자를 합성하였다. 침전은 몇 가지 음이온이 공존이온으로 존재하는데서 수행하였다. 입자의 평균크기가 $0.2{\sim}3{\mu}m$이고 독특한 입자분포를 가진 구형의 입자가 지지 음이온의 종류, 옥살산 음이온의 생성속도, 그리고 숙성시간에 따라서 형성되었다. 숙성시간이 120 min에서 용기 밑바닥에 가라앉은 barium titanyl oxalate 입자는 지지 음이온의 종류에 따라 약 $1.5{\sim}3{\mu}m$의 단일 임계크기까지 성장하였다. 고품위의 barium titanyl oxalate를 제조하기 위해 염산이온을 지지음이온으로 선택하고 반응온도를 높혀주어야함을 이로부터 만든 barium titanate의 XRD 스펙트라 및 화학분석 데이터의 검토로 알 수 있었다.