A Study on the Properties of Polyvinyl Acetate Emulsion Mixed with SBR, Polyurethane and Epoxy Latex

SBR, 폴리우레탄 및 에폭시 라텍스를 혼합한 폴리초산비닐 에멀젼 수지의 물성에 관한 연구

SBR latex, polyurethane latex and epoxy latex were separately mixed with polyvinyl acetate emulsion. The various physical properties were examined for the mixtures. Epoxy mixtures gave a transparent film. Both polyurethane and SBR mixtures showed opaque film with high viscosity. In SBR and polyurethane increase in hardness was dependent on the evaporation rate of water, but in epoxy it was dependent on the degrees of crosslink. Epoxy's showed excellent water-resistance. SBR showed a good flexural strength and impact strength. When vinyl acetate emulsion was mixed with less than 10% latex paper tube showed the ductile fracture, but over latex content 20%, it showed the brittle fracture.

폴리초산비닐 에멀젼 수지에 SBR 라텍스, 폴리우레탄 라텍스, 에폭시 라텍스를 각각 혼합하여 물리적 특성 및 기계적 특성을 조사하였다. 에폭시 수지의 상용성은 양호하였으며 건조도막은 투명하였다. 폴리우레탄과 SBR은 높은 점도를 나타내었으며 건조도막은 불투명하였다. SBR과 폴리우레탄 수지에서 경도의 증가는 물의 증발속도에 의존하였지만 에폭시 수지에서는 가교밀도의 증가에 의존하였다. 에폭시 수지는 매우 뛰어난 내수성을 나타내었다. SBR은 높은 굴곡강도와 충격강도를 나타내었다. 폴리초산비닐에 라텍스를 10% 이내로 혼합하였을 때에는 연성파괴를 나타내었고 20% 이상 혼합하였을 때에는 취성파괴를 나타내었다.