Abstract
By the mechanical alloying method Ni-W(WC) composite materials were prepared to improve the resistance for creep and sintering of Ni-anode at the operating temperature of$ 650^{\circ}C$. Amorphization was observed from the XRD analysis of mechanically alloyed powder caused by the destruction of ordered crystals. Sintering was performed at $1280^{\circ}C$ for 10 hours in $H_2$ atmosphere. From the result of dot-mapping and TEM analysis the second phase was not observed at Ni-W interface while W particles of less 0.lam were distributed finely and uniformly in Ni matrix. This finely and uniformly distributed W in Ni matrix is expected to enhance the mechanical properties of Ni-anode through the dispersion and solid solution hardening mechanisms.
MCFC(Molten Carbonate Fuel Cell) 작동온도인 $650^{\circ}C$에서 Ni 음극의 Creep 및 소결에 대한 저항성을 개선시키고자 Ni-W(WC) 복합재료를 기계적 합금법으로 제조하였다. 기계적 합금화한 분말의 XRD분석결과 밀링시간이 증가함에 따라 재료의 규칙적인 결정이 파괴되어 비정질화 되어가는 경향을 보였다. 소결은 $1280^{\circ}C$의 수소분위기에서 10시간 행하였다 소결된 시편의 dot-mapping 및 TEM 분석결과 Ni-W 계면에서의 2차상 관찰되지 않았으나 $0.1\mu\textrm{m}$ 이하의 W이 Ni 기지내에 미세하고 균일하게 분포되어 있는 것으로 나타났다. 이와같이 미세하고 균일하게 분포되어 있는 W은 고용강화 및 분산강화 효과를 통하여 Ni음극의 기계적 특성을 향상시킬 것으로 기대된다.