Abstract
Bond strength of reinforcing bar to high-perfomance concrete using belite cement is explored using beam end test specimens. The key parameters for the bond test are slump of concrete, top bar effect, and strength of concrete in addition to concrete cover. The test results show that the specimens with belite cement concrete show approximately 10% higer bond strength than those with portland cement concrete. The results also show that the bond strength from the high strength concrete is function of the square root of concrete compressive strength. Bond strength of the top bar is less than bond strength of bottom bar, but the ratios of the bond strength of bottom-cast bars to those for top-cast bars are much less than the modification factor for top reinforcement found in the ACI 318-95 code. Comparisons with other reported tests identified that belite cement increased bond strength while silica fume or flyash used in high strength concrete decreased bond strength. The high-strength and high-slump concrete with belite cement performs well in terms of bond strength to reinforcing steel.
고성능 belite 시멘트 콘크리트에 대한 부착특성에 대하여 코\ulcorner리트의 강도, 슬럼프, 배근위치, 피복두께 등의영향요인을 보단부시험체와 이음길이 보시험체를 통해 연구하였다. 동일한 압축강도의 1종 보통 포틀랜드 시멘트 콘크리트에 비해 부착강도는 약 10%증가하였고 압축강도 600kg/$\textrm{cm}^2$의고강도 belite 콘크리트에서 부착강도가 대체로 {{{{ SQRT { f'c} }} }}에 비례하였다. 유동성에 있어서 높은 슬럼프에 비해 ACI 318-95 규준에서 제시하는 상부근 계수 1.3이하의범위에 있었으며 이것은 고유동 belite 콘크리트가 블리이딩이나 골재분리가 적은 것으로 보여졌다. 또한 고강도 belite시멘트 콘크리트를 사용한 이음길이 보시험체에서 부착강도는 기존 예측식의 값보다다소 높게 나타났으며, 실리커흄, 플라이애쉬를 사용한 고강도 콘크리트 부착강도의 기존연구결과인 낮은 값과 차이를 보였다. 이상의 결과로 고유동, 고강도 belite 시멘트 콘크리트는 철근과의 부착성능이 다른 재료에 비해 양호한 것으로 나타났다.