Mechanical grinding and subsequent annealing were applied to the $Nd_5Pr_7Fe_{82}B_6$ and $Nd_{12}Fe_{82}B_6$ ingots, and the crystal structure and magnetic properties were investigated. After 330 hours milling, the particles with $2~3\mu\textrm{m}$average size were identified to be composed of very fine crystallites judging from the x-ray diffraction patterns. The intrinsic coercivity of 18.36 ~ 18.79 kOe and the maximum energy product of 8.32-8.38 MGOe were obtained by the annealing of the milled powders at $600^{\circ}C$ for 2 hours. Annealing at a higher temperature resulted in the improved magnetic properties. However it was revealed that the control of the micro-crystallites formed during the grinding process was more important to get an optimized magnetic properties than the annealing condition.
$Nd_5Pr_7Fe_{82}B_6$ 및 $Nd_{12}Fe_{82}B_6$ 조성의 1차 용유된 ingot에 대하여 기계적 분쇄처리 및 열처리를 행하고 결정구조 및 자기적 특성을 측정하였다. Ar 분위기 하에서 330시간 분쇄처리한 결과 $2~3\mu\textrm{m}$크기의 입자가 얻어졌으며, x-선 회절도로부터 각 입자는 미세한 결정립으로 구성되어 있음을 알았다. 330시간 분쇄처리된 분말을 $600^{\circ}C$에서 2시간 열처리함으로써 항자계가 18.36-18.79kOe, 최대에너지적이 8.32-8.38 MGOe인 자기적 특성을 얻었다. 열처리 온도가 높아지면 자기적 특성이 향상되었으나, 기계적 분쇄처리에 의한 ingot의 미세결정화 과정이 최적의 자기적 특성을 얻는데 더욱 중요하였다.