Abstract
(PZT, PST, PT)/ YBCO structured have been grown on single crystal $LaAlO_3$ using in-situ Nb:YAG pulsed laser deposition technique. The optimum conditions of fabrication for high quality films have been established under various oxygen pressure. TBCO was used as a metallic electrode for polarizing ferroelectric thin fillms. Lattice mismatch of these materials were found to be with in 3%. As a result XRD patterns and rocking curves, (PZT, PST, PT)/ YBCO multiayered thin films on $LaAlO_3$ substrates showed preferred orientation to c-axis. For invastigation on electrical properties of ferroelectric thin films, remanent polaiztion $P_r$ and coercive field $E_c$ were measured for three samples. At each optimum condition, they showed the values of P_r=60 \mu C/cm^2 and E_c=240kV/ cm for PT, 30\mu C/cm^2 and 105kV/cm for PZT, 1.5\mu C/cm^2$ and 15kV/cm for PST. Frequency dependence of dielectric properties of ferroelectric thin fillms was also investigated. As a result, it showed the frequency dependence was relatively small in the range of 10Hz~10kHz.