Far IR Emission and Thermal Properties of Ceramics Coated Nylon Fabrics

세라믹스 처리된 나일론 직물의 원적외선 방사성능과 보온효과

The purpose of this study was to evaluate the thermal properties of ceramics coated nylon fabrics by determining far infra-red emissive properties, heat storage/release and thermal insulation. Far IR emissivity and emissive power were measured for 7~ 140n at 50'C . Three types of ceramics such as cordierite with $\alpha$-alumina, a-alumina with titanium oxide and a-alumina were chosen as specimens. Cordierite with $\alpha$-alumina was chosen to treat on the fabrics due to the good emissive properties on the fabrics. Add-ons and contents of ceramics were analyzed for ceramics and/or polyurethane coated fabrics. For the physical properties, thickness and air permeability were measured. Results showed a difference in the emissive property between ceramics themselves and ceramics coated fabrics. In the ambient temperature, there was no diffenence in emissivity among the different ceramics contents. Thermography showed that when the fabric was heated with the light, surface mean temperatures of fabrics were increased as the contents of ceramics increased, and the heat storage property was confirmed. In case of same thickness and air permeability, the thermal insulation value increased as the contents of ceramics increased because of increasing heat storage and Far IR reflectivity. So there were absorption and heat storage of ceramics for Far IR from human and reflection to human between ceramics coated fabrics and human.