Abstract
The BaTiO3 powders extensively used as MLCC (Multilayer ceramic capacitor) in electronic ceramic in-dustry were synthesized by GNP (Glycine-Nitrate process) The powders were prepared using carbonate and alkoxide as starting materials and nitric acid was used as a solvent for starting materials as well as an oxidant for combustion. The BaTiO3 powders were synthesized using different amounts of glycine as a fuel for combustion. The characteristics of synthesized powders were examined with helium pycnometer X-ray diffraction(XRD) Brunauer-Emmett-Teller with N2 adsorption and scanning electron microscopy(SEM). It was found that single phase BaTiO3 could be formed when the as-synthesized powders were heat-treated at 100$0^{\circ}C$ When the glycine/cation molar ratio was 1,2 specific surface area was 24m2/g
MLCC(Multilayer ceramic capacitor) 등의 전자 세라믹스 분야에서 폭넓게 이용되는 BaTiO3 분말 제조를 위해 GNP(Glycine-Nitrate process)법을 이용하였다. 일반적인 GNP법과는 달리 출발물질로 카보네이트와 알콕사이드를 도입했고, 연소반응의 산화제 및 출발물질의 용매로써 질산을 사용하였으며, 연소합성시의 연료인 글리신의 첨가량을 달리하여 분말을 합성하였다. 연소합성된 분말의 특성은 helium pycnometer, XRD, N2 흡착을 이용한 BET, 주사전자현미경 등으로 분석하였다. 제조된 전구체 분말은 100$0^{\circ}C$로 하소시에 단일상의 BaTiO3 상으로 전이되었으며, 조성이 1.2인 경우 24m2/g의 높은 비표면적 값을 나타내었다.