Y$_2$O$_3$ 를 첨가한 정방정 지르코니아에서의 접촉손상 및 강도저하

Contact Damage and Strength Degradation of Yttria doped Tetragonal Zirconia Polycrystal

  • 발행 : 1998.05.01

초록

The mechanical properties and damage mode of {{{{ {Y}_{2 } {O}_{3} }}-doped tetragonal (Y-TZP) can-didated as biomaterials were performed under indentation stress-strain curve critical load for yield and cracking strength degradation and fatigue behavior with Hertzian indentation tests. This material shows the brittle behavior which is confirmed by indentation stress-strain response. The critical load for cracking(Pc) is much higher than that for yields (Py) indicating crack resistance Strength were strongly dependant on contact area and there were no degradation when the indenter size was ${\gamma}$=3.18 mm suggesting that Y-TZP should be highly damage tolerant to the blunt contacts. Multi-cycle contact were found to be innocuous up to {{{{ {10 }^{6 } }} cycles at 500N and {{{{ {10 }^{5 } }} cycles at 1000N in water. On the other hand contacts at {{{{ {10 }^{6 } }} cycles at 1000 N in water did show some signs of incipient degradation. By contrast contacts with Vickers indenter pro-duced substantial strength losses at much lower loads suggesting that the mechanical integrity of this ma-terial would be compromised by inadvertent sharp contacts.

키워드

참고문헌

  1. Compendium v.17 no.8 Dental Ceramic Restorative Systems R.A.Giordano
  2. J.Mater .Sci. v.13 Effect of Stress-Induced Phase Transformation on the Properties of Ploycrystalline Zirconia Containing Metastable Tetragonal Phase T.K.Gupta;F.F.Lange;J.H.Bcchtold
  3. J.Am.Ceram.Soc. v.72 no.4 In Vitro Agening of Yttria-Stabilized Zirconia J.L.Drummond
  4. J.Biomed.Mater.Res. v.34 Fatigue Behavior of Zirconia Hip Joint Heads:Experimental Results and Finite Element Analysis J.M.Drouin;B.Cales;J.Chevalier;G.Fantozzi
  5. Biomaterial v.11 Mechanical Behavior of Zirconia and Zirconia Toughened Alumina in a Simulated Body Environment I.Thompson;R.D.Rawlings
  6. J.Mater.Sci. v.17 Transformation Toughening, Part 3 F.F.Lange
  7. Annu,Rev.Mater.Sci. v.24 Progress in Transformation Toughening of Ceramics R.H.J.Hannink;MV Swain
  8. J.Am.Ceram.Soc. v.78 no.4 Hertzian Contact Damage in Magnesia-Partially-Stabilized Zirconia A.Pajares;F.Guiberteau;B.R.Lawn;S.Lathabai
  9. J.Mater.Res. v.10 no.10 Damage Accumulation and Cyclic Fatigue in Mg-PSZ at Hertzian Contacts A.Pajares;L.Wei;B.R.Lawn;D.B.Marshall
  10. J.Mater.Sci. v.26 Low Temperature Degradation of Y-TZP Materials J.J.Swab
  11. J.Am.Ceram.Soc. v.68 Strength Recovery in Degraded Yttria Doped Zirconia Polycrystals R.L.K.Matsumoto
  12. J.Am.Ceram.Soc. v.79 no.10 Stress Analysis of Contact Deformation in Quasi-Plastic Ceramics A.C.Fischer-Cripps;B.R.Lawn
  13. Hardness of Metals D.Tabor
  14. J.Am.Ceram.Soc. v.64 no.19 A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness:1.Direct Crack Measurements G.R.Anstis;P Chantikul;D.B.Marshall;B.R.Lawn
  15. J.Acous.Soc.Am. v.33 Pulse-Superposition Methods for Measuring Ultrasonic Wave Velocities in Solids H.J.McSkimin
  16. Symposium on Dynamic Modulus Measurements The Pulsed Ultrasonic Velocity Method for Detemining Material Dynamic Elastic Moduli G.V.Blessing;Wolfenden A(ed.)
  17. J.Am.Ceram.Soc. v.77 no.7 Effect of Grain Size on Hertzian Contact in Alumina F.Guiberteau F;N.P.Padture;B.R.Lawn
  18. J.Am.Ceram.Soc. v.80 no.9 Role of Microstructure in Hertzian Contact Damage in Silicon Nitride:Ⅰ, Mechanical Characterization S.K.Lee;S.Wuttiphan;B.R.Lawn
  19. J.Am.Ceram.Soc. v.65 no.9-10 Flaw Characteristics in Dynamic Fatigue:The Influence of Residual Contact Stresses D.B.Marshall;B.R.Lawn
  20. Theory of Elasticity S.Timoshenko;J.N.Goodier
  21. J Mater.Sci. v.29 Trapped Cracks at Indentations R.F.Cook;L.M.Braun;W.R.Cannon
  22. Fracture of Brittle Solids(Second Edition) B.R.Lawn
  23. J.Dent.Res. Mechanical Characterization of Dental Ceramics Using Hertzian Contacts I.M.Peterson;A.Pajares;B.R.Lawn;V.P.Thompson;E.D.Rekow
  24. J.Am.Ceram.Soc. v.58 no.9-10 Strength Degradation of Brittle Surfaces:Blunt Indenters B.R.Lawn;S.M.Wiederhom;H.Johnson
  25. J.Am.Ceram.Soc. v.50 no.8 Influence of Water Vapor on Crack Propagation in Soda-Lime Glass S.M.Wiederhorn
  26. Philos.Mag. v.A68 no.5 Indentation Fatigue: A Simple Cyclic Hertzian Test for Measuring Damage Accumulation in Polycrystal Ceramics F.Guiberteau;N.P.Padture;H.Cai;B.R.Lawn
  27. Friction and Wear of Ceramics Surface Damage and Mehanics of Fretting wear in Ceramics P.J.Kennedy;A.A.Conte;E.P.Whitenton;L.K.Ives;M.B.Peterson;S.Jahanmir(ed.)