Transition Temperature Evaluation of 1Cr-1Mo-0.25V Steel Using Miniaturized Charpy Impact Specimen

소형 샤르피 충격시험편을 이용한 1Cr-1Mo-0.25V강의 천이온도 평가

  • Nahm Seung Hoon (Failure Prevention Research Center, Korea Research Institute of Standards and Science) ;
  • Kim Si Cheon (Failure Prevention Research Center, Korea Research Institute of Standards and Science) ;
  • Lee Hae Moo (Failure Prevention Research Center, Korea Research Institute of Standards and Science)
  • 남승훈 (한국표준과학연구원 방재기술연구센터) ;
  • 김시천 (한국표준과학연구원 방재기술연구센터) ;
  • 이해무 (한국표준과학연구원 방재기술연구센터)
  • Published : 1998.12.01
Download PDF
⟨ Previous Next ⟩

Abstract

Miniaturized specimen technology Permits mechanical behavior to be determined using a minimum volume of material. The technology is useful in case of not collecting a large amount of materials from industrial equipments. Five kinds of accelerated degradation materials were prepared by isothermal aging heat treatment at $630^{\circ}C$. Three kinds of specimens were prepared for impact testing. In order to increase plastic constraint of subsize specimen, side-groove was introduced. Results between subsize and full size impact testing were compared. Size effects correlations were developed for the impact properties of turbine rotor material. These correlations successfully predict the ductile brittle transition temperature (DBTT) of full size Charpy impact specimens based on subsize specimen data.

소형 시험편 기술은 최소량의 재료를 사용하여 그 재료의 물리적인 거동을 특성화할 수 있기 때문에 산업설비로부터 많은 재료를 수집할 수 없는 경우에 유용한 방법이다. 본 연구에서 사용한 재료는 화력발전소 터빈로터 소재로 많이 사용되고 있는 1Cr-1Mo-0.25V강이었으며, $^630{\circ}C$에서 등온열화처리하여 5종류의 가속 열화 모사재를 만들었다. 충격시험에는 표준 시험편과 소형 시험편이 사용되었으며, 일부 소형 시험편에 소성 구속을 증가시키기 위해 측면흠을 만들어 넣었다. 표준 시험편과 소형 시험편의 충격특성을 비교하였으며 크기효과를 고찰하였고, 소형 시험편의 연성취성천이온도와 표준 시험편의 연성취성천이온도와의 상관관계를 만들었다. 따라서 소형 시험편의 충격시험결과로부터 표준 시험편의 충격특성을 추정하는 것이 가능하게 되었다.