High Temperature Oxidation Behavior of the Brazed Joint in Fe-Cr-Al-Y Alloy

Fe-Cr-AI-Y합금에서 브레이징 접합부의 고온산화거동

  • 문병기 (한국기계연구원 재료공정연구부) ;
  • 최철진 (한국기계연구원 재료공정연구부) ;
  • 박원욱 (한국기계연구원 재료공정연구부)
  • Published : 1997.12.30

Abstract

To improve the joining characteristics of metallic converter substrate for exhaust gas cleaning, high temperature brazing process has been studied. In this study, the effect of chemical composition of brazing filler metal on the oxidation behavior of brazed joints was investigated closely. Brazing was carried out at $1200^\circC$ in vacuum furnace using nickel-based filler metals : BNi-5 powder(Ni-Cr-Si base alloy) and MBF-50 foil(Ni-Cr-Si-B). The MBF-50 containing 1-1.5 wt%B showed relatively poor oxidation resistance of the brazed joints compared to BNi-5, because of the faster invasion of oxygen through the Kirkendal voids along the interface of mother alloy/filler metal.

본 연구에서는 배기 가스 촉매정화용 금속담체 지지체의 접합특성을 향상시키기 위하여, 브레이징 접합부의 고온내산화성에 미치는 브레이징 합금원소의 영향을 고찰하였다. 브레이징은 Ni계 합금인 BNi-5 분말(Ni-Cr-Si계합금)과 MBF-50 foil(Ni-Cr-Si-B계 합금)을 사용하여 $1200^\circC$의 진공중에서 행하였다. 약 1-1.5 wt%의 B을 함유한 MBF-50으로 브레이징된 시편이 BNi-5로 브레이징된 시편에 비해 내산화성이 떨어지는 것으로 나타났으며. 이것은 합금/브레이징 계변을 따라 형성된 Kirkendall void를 통한 산소의 빠른 침투로 인한 것으로 생각된다.

Keywords