The Decomposition of Cyanide by the Electrodeposited Lead Dioxide Electrode

전착이산화납전극에 의한 시안염 분해

${\beta}-PbO_2$ electrode, which was electrodeposited on Ti madras, was prepared and for the decomposition of cyanide in electroplating wastewater. After the investigation of temperature and pH conditions for no hydrogen cyanide evolution during the decomposition of cyanide, the optimum current densities of ${\beta}-PbO_2$ electrodeposition and cyanide decomposition were determined in 500ppm NaCN solution, and durability of ${\beta}-PbO_2$ electrode was also investigated. Hydrogen cyanide was actively generated above $40^{\circ}C$ and was not evolved above pH 13. ${\beta}-PbO_2$ electrode electodeposited at $5A/dm^2$ showed the best cyanide decomposition efficiency The decompostion efficiency was about 70% at low decomposition current density ($0.08A/dm^2$), and it decreased gradually to about 10% as the decomposition current density increased up to $4A/dm^2$. The film of ${\beta}-PbO_2$ electrodeposited was corrosive at $20A/dm^2$ and was broken at $50A/dm^2$.

마드래스형 티타늄 기판위에 전착시킨 $\beta$형-이산화납 전극을 이용하여 도금폐수중의 시안염을 분해하기 위한 최적조건에 관하여 검토하고자 하였다. 시안분해에 알맞는 온도 및 pH를 검토한 후 500ppm NaCN을 전해질로 하여 시안분해효율이 높아질 수 있는 이산화납의 전착전류밀도와 시안의 분해전류밀도를 구하였으며, 이산화납 전극의 내구성을 조사하였다. 시안화수소의 발생은 온도 $40^{\circ}C$이상의 시안염용액에서 활발했으며 pH 13이상에서는 시안화수소가 발생하지 않았다. $5A/dm^2$의 전류밀도로 전착시킨 이산화납전극에서 최대의 시안분해효율을 나타냈다. $0.08A/dm^2$의 시안분해전류밀도에서 약 70%의 시안분해 전류효율을 보였으며 $4A/dm^2$이상에서는 약 10% 정도로 일정해지는 경향을 보였다. 이산화납 전착층은 약 $20A/dm^2$의 시안분해 전류밀도에서부터 열화가 일어났으며 약 $50A/dm^2$에서 파괴되었다.