A STUDY ON FRACTURE STRENGTH OF CONVENTIONAL AND COPY-MILLED IN-CERAM CROWNS

Copy-milled Celay In-Ceram 전부도재관의 파절강도에 관한 연구

The purpose of this study was to compare the fracture resistance of copy-milled and conventional In-Ceram crown. Four groups of ten uniform sized all-ceramic crowns were fabricated. In-Ceram Spinell and In-Ceram Alumina crowns were fabricated as control group, Celay In-Ceram Spinell and Celay In-Ceram Alumina crowns were fabricated as test group. All specimen were cemented on stainless steel master die with resin cement, and stored in $37^{\circ}C$ water for 1 day prior to loading in Instron testing machine. Using a steel ball at a crosshead surfed of 0.5mm/min, the crowns were loaded at $30^{\circ}C$ angle until catastrophic failure occurred. The results obtained were as follows : 1. With the value of $984.8N{\pm}103.67N$, the strength of Celay In-Ceram Alumina crowns had a significantly higher fracture strength than conventional In-Ceram Alumina crowns ($876.2N{\pm}92.20N$) (P<0.05) 2. The fracture strength of Celay In-Ceram Spinell crowns($706.3{\pm}70.59N$) was greater than that of conventional In-Ceram Spinell crowns($687.4{\pm}90.26N$), but there was no significant difference(P>0.05). 3. The In-Ceram Alumina crowns had a significantly higher fracture strength than In-Ceram Spinell crowns in both methods(P<0.05). 4. Ther order of fracture strength was as followed : Celay In-Ceram Alumina, In-Ceram Alumina, Celay In-Ceram Spinell and In-Ceram Spinell crowns