원심주조한 Cu-Zn-Al계 합금의 기계적 성질에 미치는 Ti 첨가와 균질화 처리의 영향

Effects of Ti Addition and Homogenizing Heat Treatment on the Mechanical Properties of Centrifugal Cast Cu-Zn-Al Alloy

Effects of Ti addition and homogenizing heat treatment on the mechanical properties in Cu-Zn-Al alloy (high strength yellow brass) were investigated. Grain refinement was successfully achieved by Ti addition. The microstructure, which was composed of island or fine feather-like branched Ti compounds was changed to feather-like eutectic microstructure as the content of Ti increased. The highest hardness value was obtained for 0.5 wt.% Ti specimen and the second was Ti non-added specimen in as-cast condition. The highest tensile strength was obtained for 0.5 wt.% Ti specimen. Because of the presence of cast defects and worse castability, tensile strength decreased as the content of Ti increased. Elongation increased with increasing homogenizing time and temperature; remarkable increase was obtained for $400^{\circ}C$ homogenizing temperature in the 0.5 wt.% Ti specimen. For $500^{\circ}C$ and $600^{\circ}C$ homhgenizing, temperature, high elongation was obtained in 2 and 4 wt.% Ti specimen.