A Study on the Characterization of Intrinsic Flame Retardant and Heat Resistant Sulfur-Bridged Heterocyclic Polymers

본질적 난연 및 내열성 헤테로환식 폴리머의 특성에 관한 연구

The intrinsic flame retardant and heat resistant polymers such as PQXS [poly( quinoxaline )sulfide], PIQS [poly(isoquinoline)sulfide] and PQS [poly(quinoline)sulfide] were synthesized from 2, 3-dichloroquinoxaline, 1, 3-dichloroisoquinoline and 4, 7-dichloroquinoline. They were characterized by FT-IR, UV/Vis spectroscopy, DTA and elemental analysis. The melting point above $350^{\circ}C$ of the polymers show higher than that of the heat resistant PPS polymer(mp. $295^{\circ}C$), In the LOI test, the polymers exhibit an intrinsically high flame retardant property having the LOI values in the range of 41~42. The vertical burning test for the polymers also show an UL 94 V-0 performance.

본질적인 난연 및 내열성의 PQXS, PIQS, PQS 3종류의 폴리머를 2,3-dichloroquinoxaline, 1,3-dichloroisoquinoline, 4,7-dichloroquinoline을 각각 출발 물질로 하여 합성하였다. 이들을 FT-IR, UV/Vis 분광분석, DTA, 원소분석 등에 따라 특성분석을 행하였다. 이들 폴리머소재는 내열 및 난연특성 시험에서 녹는점 기준 $350^{\circ}C$ 이상의 높은 내열성과 LOI값 기준으로 41~42의 높은 수치의 난연특성을 나타내었으며 또한 수직연소시험에서 UL 94 V-0 등급의 높은 난연특성을 나타내었다.