The Fabrication of PVDF Organic Thin Films by Physical Vapor Deposition Method and Their Electrical Conductivity Phenomena

진공증착법을 이용한 PVDF 유기박막의 제조와 전기전도현상

In this study, the PVDF organic thin film was fabricated by the physical vapor deposition method to be dry-process. The distance of heat source and substrate was 5[cm] and the temperature of substrate was 30[.deg. C], when the pressure had reached 2.0 x 10$^{-5}$ [Torr], the temperature of heat source was reached to 285[.deg. C] to heat at 6-8[.deg. C/min] rate, the shutter was opened and deposition was started. TG-DTA(Thermogravimetric-Differential Thermal Analysis) spectrum of PVDF pellets showed that endothermic peak arose at 170[.deg. C] and exothermic peak at 524[.deg. C], but that of thin PVDF film showed that endothermic peak arose at 145[.deg. C] and exothermic peak at 443[.deg C]. The current density was increased linearly with increasing voltage but increased nonlinearly with higher electric field than 250[kV/cm] and activation energy was about 0.667[eV] at the temperature of 30-90[.deg. C].