There exists a certain functional relation between Vickers hardness and flow stress in the strain-hardened material. Using this relation, the Vickers hardness values in the strain-hardened material can be converted into the flow stress values in good approximation. Therefore, the information about the flow stress distribution in the material can be easily acquired through a forming experiment. That makes it possible to simulate the process state for a critical moment of cold forging under the given boundary conditions very quickly without calculating the foregoing history of the actual deformation from the beginning.