Abstract
Effects of Co thickness on the formation of epitaxial $CoSi_2$ from the Co/Ti bilayer have been investigated. Ti and Co were sequentially deposited with the Ti thickness fixed at 5 or 10nm, while the Co thickness was varied from 5 to 30nm. The metal-deposited samples were then rapidly thermal-annealed in $N_2$ at $900^{\circ}C$ for 20 sec. Material properties of $CoSi_2$ thin films were analyzed by the 4-point probe, XRD, AES, andXTEM. When the as-deposited Co thickness was below 15nm, the $CoSi_2$ with high resistivity and rough interface was formed. On the other hand, when the Co thickness was above 15 nm, the epitaxial $CoSi_2$ with the resistivity of about 16 ~ 19 $\mu\Omega.cm$, uniform composition and thickness and flat interface was formed. Initial Ti thickness has sizable effect on the formation of $CoSi_2$, when the Co layer was very thin (~ 5 nm). But there was no significant effect of the Ti thickness for the initial Co thickness of above 15 nm.