Macrostructural characteristic of the transverse cracks and fatigue behavior were studied for EH 32 TMCP 50mm thick plate welded with FACW under the variation in preheat and interpass temperatures. Transverse cracks were detected in specimen welded with preheat and interpass temperature below $30^{\circ}C$, but cracks were not detected in the specimens welded with preheat and interpass temperatures at the range of $100~120^{\circ}C$.C. The location of crack formation was found to strongly depend upon the thickness of weld layers as regard to the plate thickness.