MOVPE GROWTH OF HgCdTe EPILAYER WITH ARSENIC DOPING

We report on p-type arsenic doping of metalorganic vapor phase epitaxially (MOVPE) grown HgCdTe on (100) GaAs. HgCdTe was grown at $370^{\circ}C$ in a horizontal reactor with using dimethy-cadmium, diisoprophyltelluride, and elemental Hg. We used tris-dimethylaminoarsenic (DMAAs) as the metalorganic for p-doping. 4micron thick CdTe and subsequently 10micron thick HgCdTe were grown on (100) GaAs substrate. Interdiffused multilayer process in which thin CdTe and HgTe layers are grown alternately and interdiffused to obtain homogeneous HgCdTe alloys was used. Arsenic was doped during CdTe growth cycle. After growth HgCdTe was annealed at $415^{\circ}C$ for 15 min and then annealed again at $220^{\circ}C$ for 3 hr, both with Hg-saturate condition. We could obtain p-doping from 2.5$\times$$10^{16}$ to 6.6$\times$$10^{17}$$cm^{-3}$, depending on the DMAAs partial pressure. With the dual Hg-annealing, activation of arsenic was aboutt 90%, which was confirmed by SIMS measurement. With only low temperature annealing at $220^{\circ}C$ for 3hr, activation efficiency was about 50%.