5, 100 mtorr의 증착압력에서 스퍼터 증착한 구리박막층이 Cu/Cr 박막과 폴리이미드 사이의 접착력에 미치는 영향
The effects of Cu thin films sputter deposited at 5 and 100 mtorr on the adhesion between Cu/Cr film and polyimide
초록
The effects of microstructural change on the adhesion strength between Cu/Cr film and polyimide have been studied. Cr films (50 nm thick) and Cu films (500 or 1000 nm thick) were deposited on polyimide by DC magnetron sputtering. During Cu deposition the Ar pressure was 5 or 100 mtorr. The microstructure was observed by SEM and the adhesion was measured by T-peel test. Plastic deformation of peeled metal strips was characterized quantitatively by using XRD technique. The film in which Cu is deposited at 100 mtorr has higher adhesion strength than the film in which Cu is deposited at 5 mtorr. And in the film with same deposition pressure of 100 mtorr, the adhesion strength is increased as the deposited thickness increases from 500 to 1000 nm. The adhesion change of Cu/Cr can be interpreted as the difference in plastic deformation.
키워드