A Study on the Effect of Accelerated Curing on 28-Days Compressive Strength of Concrete

촉진양생이 콘크리트의 28일 압축강도에 미치는 영향에 관한 연구

The pulished works on Accelerated Curing Effect were generally performed around from 1960 to 1970th century for 18 to 24 hours - total curing periods. It is not possible to define the effect of temperature rise because those results were obtaine mainly by using the manually operated steam-curing tank. Thus, it may not be available to apply those data immediately on the domestic PC wall production line. The testing specimens were made from the standard mix proportion according to those of domestic PC factories to establish a basic data for the Accelerated Curing Effect. The experimental tests were conducted according to the conditions of each sub-curing periods. By comparing the results of compression tests on de-molded and 28-day water-curing specimens, we find that the most effective curing condition to obtain more than the required design strength after 28 day of water curing may be as follows: the presteaming period does not affect seriously and less than$30^{circ}C/hr$- the rate of temperature rise andless than $82^{circ}C$ - maximum temperature are necessary. It seems that post-curing procedure is very important factor to increase the effect of accelerated curing.

기존의 촉진양생 연구는 1960~1970년대에 주로 실행된 것으로, 전체 증기양생기간이 18시간 또는 24시간인 경우에 대하여 연구되었고, 상기 연구 결과는 수동식 항온항습조를 사용하였으므로 온도상승구배의 효과에 대하여 명확한 규명을 할 수 없다고 판단되었다. 따라서 국내 PC공장 여건에서 그 직접적인 적용이 불가능한 실정이다. 본 연구는 효과적인 콘크리트 촉진양생에 대한 기본 자료를 정립할 목적으로, 국내 PC 공장에서 사용하는 배합표를 근거로 시험공시체를 제작한 후, 각 해당 양생주기 조건을 변화시켜 가면서 실험하였다. 탈형시 및 수중양생 재령28일의 측정하고 비교 검토한 결과, 재령 28일 후 설계강도값을 초과하는 가장 효과적인 촉진양생조건, 본 실험조건 하에서 전양생시간은 커다란 영향을 미치지 않았으며, 온도상승구배는 $30^{circ}C/hr$ 이하로, 최고양생온도는 $82^{\circ}C$이하로 양생해야 하며, 또한 촉진양생 후 2차 양생으로 강도증진을 도모함이 촉진양생의 효과를 증대시킬 수 있다고 판단되었다.