Magnetoresistance of ${[Co/Fe/Cu]}_20$ Multilayers

${[Co/Fe/Cu]}_20$ 다층박막의 자기저항 특성

  • Published : 1996.12.01

Abstract

We have studied the effect of a spin-dependence interface electron scattering on the giant magnetoresistance by adding a Fe magnetic material to the Co/Cu interfaces. The $Fe(50\;{\AA})/[Co(17\;{\AA})/Fe(t\;{\AA})/Cu(24\;{\AA})]_{20}$ multilayers are deposited on the Corning glass 2948 and 7059 substrates in a dc magnetron sputtering system. The magnetoresistance ratio is 22 % in the only Co/Cu multilayer, while it is increased to 26 % with inserted ultra thin Fe interface layer and reduced with increasing thickness of the Fe interface layer. It was investigated to the dependence of the magnetoresistance behaviors on annealing temperature. The magnetic properties of the multilayers were measured by vibrating sample magnetometer. Also, the structures and the surface roughness of samples were characterized by X-ray diffraction and atomic force microscope, respectively. The magnetoresistance ratio was increased to annealing temperature $300^{\circ}C$, but reduced at the temperature higher than $300^{\circ}C$ due to the interfacial diffuse.

본 연구에서는 dc magnetron sputtering 방법으로 Corning glass 위에 자성층 Co와 비자성층 Cu의 계면에 얇은 Fe 자성층을 삽입하여 다층박막 $Fe(50\;{\AA})/[Co(17\;{\AA})/Fe(t\;{\AA})/Cu(24\;{\AA})]_{20}$을 제작하고 Fe 두께와 열처리 온도에 따른 자기저항 변화를 관찰하였다. 시료진동형자기계로 자기이력곡선을 측정하여 자기적 성질을 조사하였고 구조 및 표면 분석을 위해 각각 X-선 회절장치와 AFM(Atomic Force Microscope)을 이용하였다. 얇은 Fe 사이층을 삽입하지 않은 Co/Cu 다층박막에서 자기저항비가 22%인데 비해 얇은 Fe층을 삽입하였을때는 자기저항비가 26%까지 증가하였고 Fe 사이층의 두께가 점차 두꺼워짐에 따라 자기저항비는 다시 감소함을 나타냈다. $300^{\circ}C$ 까지 열처리한 결과 자기저항비는 증가하였으나 그 이상의 온도에서는 감소하였다.

Keywords