Piezoelectric properties of porous PZT ceramics for hydrophone Applications

수중청음기 응용을 위한 다공질 PZT 세라믹스의 압전특성

PZT powders were prepared by the molten salt synthesis method. The porous PZT ceramics were made from a mixture of PZT and polyvinylalcohol(PVA) by BURPS(Burnout Plastic Sphere) technique. The porous PZT bodies were fabricated from the green compacts with various amounts of PVA spheres. The piezoelectric coefficient d$_{33}$ (334~350*10$^{-12}$ C/N)of porous PZT ceramics(364*10$^{-12}$ C/N). The figure of merit(d$_{h}$g$_{h}$) of porous PZT specimens evaluating the sensitivity for ultrasonic transducer applications was improved significantly(11~70times) in comparison with that of single phase PZT ceramics(100*10$^{-15}$ m$^{2}$/N). The thickness mode coupling factor k$_{t}$(0.5~0.6) of porous specimens was comparable with that of single phase PZT ceramics(k$_{t}$=0.7). The mechanical quality factor of porous PZT specimens was smaller than 10, and thus these porous PZT ceramics would be believed as a good candidate for broad band hydrophone applications. (author). 10 refs., 7 figs.igs.igs.