A STUDY ON THE SHEAR BOND STRENGTH OF THE COMPOSITE RESIN TO GLASS IONOMER CEMENT ACCORDING TO SURFACE TREATMENT METHODS OF GLASS IONOMER CEMENT

글라스 아이오노머 시멘트의 표면처리방법에 따른 복합레진과의 전단결합강도에 관한 연구

  • No, Bong-Hwan (Department of Conservative Dentistry, College Dentistry, Chosun University) ;
  • Hwang, Ho-Keel (Department of Conservative Dentistry, College Dentistry, Chosun University) ;
  • Cho, Young-Gon (Department of Conservative Dentistry, College Dentistry, Chosun University)
  • 노봉환 (조선대학교 치과대학 보존학교실) ;
  • 황호길 (조선대학교 치과대학 보존학교실) ;
  • 조영곤 (조선대학교 치과대학 보존학교실)
  • Published : 1995.03.10

Abstract

The purpose of this study was to evaluate the shear bond strength between composite resin and glass ionomer cement according to surface treatment methods of glass ionomer cement. Sixty round acrylic cylinders were fabricated. And then, a round undercut cavity(8 mm diameter, 2.5mm depth) was prepared in the center of the every acrylic cylinder. After all cavities were restored by using light-cured glass ionomer cement. A total of sixty acrylic cylinders restored with glass ionomer cement were divided into 4 groups according to surface treatment methods of glass ionomer cement. The surface treatment of each group were as follows : control group : no treatment Group 1 : acid etching Group 2 : sandblasting Group 3 : air-podwer abrasive polishing The composite resin was bonded to glass ionomer cement of each specimens. And the shear bond strength was tested with a universal testing machine at a cross-head speed of 1mm/min and 500kg in full scale. The results were as follows : 1. The sandblasting group(group 2) had the highest shear bond strength with $272.50{\pm}24.96\;kg/cm_2$ and the acid etching group(group 1) had the lowest shear bond strength with $192.89{\pm}29.32kg/cm_2$. 2. The no treated group(control group) had higher shear bond strength than acid etching group(group 1) (p<0.05). 3. The sandblasting group(group 2), air-powder abrasive polishing group(group 3) and no treated group(control group) had higher shear bond strength than the acid etching group(group 1) (p<0.05). 4. The sandblasting group(group 2) and air-powder abrasive polishing group(group 3) had higher shear bond strength than the no treatment group(control group), but there was not significant(p>0.05).