The Effect of Ageing on Grain Refinement of CuAlNi Shape Memory Alloy

CuAlNi 형상기억합금의 결정립 미세화에 따른 시효효과

This research was performed to investigate the effect of ageing on grain refinement of 82wt%Cu-13.5wt%Al-4.5wt%Ni-0.1wt% misch metal alloy with ageing temperature and time. The results obtained in this study are as follows; The variation of transformation temperature with ageing temperature had very influence on ageing time at $300^{\circ}C$. But it had not influence on ageing time at $100^{\circ}C$. The variation of transformation temperature after second reversed transformation cycle was not occured in martensitic phase ageing, but $M_s$ point was appeared equally with third reversed transformation cycle in parent phase ageing. The variation of $M_s$ point was not nearly with ageing time at $100^{\circ}C$ ageing temperature. But it was decreasing with ageing time at $300^{\circ}C$ ageing temperature and $A_s$ point was increasing with ageing time. Structure of parent phase ageing was being M18R martensitic and N2H martensitic phase. It was found that ${\alpha}$ and ${\gamma}_2$ phase were created by ageing of long time at $300^{\circ}C$ ageing temperature.