Abstract
Electroetching rates of $FeCl_3$ solution were increased according to increasing solution temperature. Activation energy of electroetching at Be'36 and 5A/$dm^2$ condition was 28.3Kcal and also, at Be'46 and 5A/dm$^2$ condition was 33.2Kcal. At Be'36 concentration of $FeCl_3$ solution, electroetching rate were more higher than at Be'46 concentration. Surfaces of etched grooves obtained at 8A/$dm^2$ or higher current density in 46 Be' concentration of $FeCl_3$ solution were observed to be flat and smooth owing to suppressing chemical etching reaction. Distinctly etched boundaries became to be appeared at 2A/$dm^2$ in Be'41 electroetching condition by differential effects. In case of applying 8A/$dm^2$ current density to Be'46 of $FeCl_3$ solution, etching depth were 4 times and side etching were 6 times more than chemical etching case respectively.