Abstract
Ag-doped $Y_1$Ba$_2$Cu$_3$O$_{7-y}$ samples have been prepared by solid state reaction. High-Tc super conductivity, microstructure and mechanical property of the Ag-doped $Y_1$Ba$_2$Cu$_3$O$_{7-y}$ samples have been studied. As the Ag content increased, the grain size of $Y_1$Ba$_2$Cu$_3$O$_{7-y}$, increased and connectivity between the grains was improved, and the sample becomed denser and harder than the undoped. From the result, it is concluded that Ag addition reduced weak link and weak coupling between grains and led to the strong coupling. Furthermore, the anisotropy of crytstal structure was decreased and thermal stability, mechanical property of $Y_1$Ba$_2$Cu$_3$O$_{7-y}$-Ag were improved.mproved.
Ag를 $Y_1$Ba$_2$Cu$_3$O$_{7-y}$에 첨가하여 고상반응법으로 시료를 제작, Ag가 $Y_1$Ba$_2$Cu$_3$O$_{7-y}$의 고온초전도성과 그의 미세구조에 미치는 영향을 조사하였고 그에 따른 기계적 특성을 연구하였다. Ag의양이 증가함에 따라 결정립의 크기가 증가하였고 연결성이 향상되어 시료의 결정구조가 치밀해지고 단단해졌으며 결정립간의 weak link와 weak coupling을 줄이고 균일한 초전도 상을 형성시킨다는 것을 알 수 있었다. 또한 $Y_1$Ba$_2$Cu$_3$O$_{7-y}$결정구조의 이방성을 줄였고 $Y_1$Ba$_2$Cu$_3$O$_{7-y}$의 열적 안정성을 향상 시켰음을 알 수 있었다. 그리고 Ag의 첨가에 따라 시료의 기계적 강도가 증가함을 보였다.가함을 보였다.