Preparation of High Range Water Reducer Containing Carboxylic Acid and Their Cement Absorptivity(I)

카르본산계 고성능감수제의 제조 및 그들의 시멘트 흡착성(I)

Styrene-Maleic anhydride copolymer (SMA) was prepared by the radical copolmerization of styrene and maleic anhydride using ${\alpha}-{\alpha}'$ azobis(isobutyronitrile) as an initiatrr. SMA was further reacted with m-amino phenol to obtain aminophenol-substituted SMR (mSMA). Sulfonated SMA and mSMA were also prepared by the reaction of copolymers with sulfuric acid The copolyniers were characterized by infrared spectroscopy. It was found from the results of elemental analysis that the substitution degree of aminophenol in the mSMR is 44% and the degree is lowered to 35% after sulfonation. The percentage of copolymers adsorbed on the surface of cement particles was increased with a decrease of added copolymers. While, the arnourit of sulfonated SMA absorbed on the surface of cement particles was larger than that of the sulfonated mSMA The copolymers synthesized in this study are probably expected as a high range water reducer for coiicxte.

스티렌과 무수말레인산의 라디칼 공중합에 의해 스티렌-무수말레인산 공중합체(SMA)를 합성하고 SMA를 m-amino phenol과 치환반응하여 m-amino phenol 이 치환된 스티렌-무수말레인산 공중합체(mSMA)도 합성하였다. 합성한 SMA와 mSMA를 황산화하여 각각 황산화 SMA(SSMA) 및 황산화 mSMA(SmSMA)를 제조하였다. 공중합체의 합성은 적외분광스펙트럼의 특성피크로부터 확인할 수 있었다. 원소분석 결과 mSMA의 m-amino phenol의 치환율은 44%이었고 이것은 황산화 과정을 거치면서 35%로 감소하였다. 공중합체의 시멘트에 대한 흡착실험 결과 공중합체의 첨가량이 적을수록 흡착율이 높게 나타났고, 첨가량에 관계없이 SSMA의 흡착율이 SmSMA의 그것보다 크게 나타났다. 본 연구에서 합성한 공중합체 (SSMA, SmSMA)는 시멘트 분산제로서의 가능성이 기대되어진다.