Improving Performance of Recycled Waste Concrete

재생 폐콘크리트의 성능향상에 관한 연구

A method for lmprovlng strengths of recycled concrete was studied to make use of it in nolmal concrete structures. Recycled conc~ete was prepared by replacing 50% by weight of coarse aggregate with recycled aggregate. Mix design rnet hod for crushed aggregates was used and specirriens were cured by normal moisture curing method. A plastlciser and a fly ash were added to the mix to improve performance of recycled concrete. Compressive strength, flexural strength, tensile strength, elastic modulus, stress-strain relationship, long-term compressive strength and fracture toughness were evaluated and compared with those of rlormal concretes. Recycled concrete showed, in general, lower compressive strength than normal concreks. It also showed lower elastic modulus, lower tensile and flexural strengths, and higher strain under the same stress level. However, by reducing w /c ratio down to 35% using the plasticiser. average compressive strength(${\alpha}_{28}$) of recycled concrete was reached. with slump of $16{\pm}2$cm, to $225kg/cm^2$ or hlgher, which is an acceptable strmgth level for normal structural concrete. I-Iowevei., elastic modulus and strain should be improved further for practical use of recycled concrctc: in normal structure. Fly ash addition in both concretes showed an effect of irnprovilig long term compressive strength and reducing strengths.

본 연구는 천연 굵은 골재 50%를 재생골재로 대치시켜 제조한 재생콘크리트를 일반 구조물에 사용할 수 있도록 성능을 향상시키기 위한 연구의 일환으로 수행되었다. 쇄석골재 사용시의 배합설계 방법으로 콘크리트를 제조하였고 일반적인 수중양생으로 공시체를 야생하였다. 재생콘크리트의 성능향상을 목적으로 유동화제와 플라이애쉬를 첨가하였다. 압축강도 등 각종 강도와 파괴인성 등을 측정하여 이를 일반콘크리트와 비교한 결과 재생콘크리트는 강도와 탄성계수가 낮고 변형율이 크며 파괴인성도 낮았다. 그러나 유동화제의 사용으로 물-시멘트비를 35%까지 낮추므로써 슬럼프 $16{\pm}2$cm에서 일반 구조물에 소요 압축강도보다 높은$225kg/cm^2$이상의 압축강도를 얻었다. 하지만 재생콘크리트를 일반 구조물에 사용을 위해서는 탄성계수와 변형율에 대한 향상이 필요하다. 또한 플라이애쉬의 사용은 장기 강도 증진 효과를 보이는 반면 강도 저하를 유발했다.